00042 CO2 AND H2S CORROSION OF API 5L-B AND 5L-X52 GRADE STEELS

Product Number: 51300-00042-SG
ISBN: 00042 2000 CP
Author: J.J. Perdomo, J.L. Morales, A. Viloria, A.J. Lusinchi
Publication Date: 2000
$0.00
$20.00
$20.00
Corrosion behavior of American Petroleum Institute (API) 5L grade B and X52 steels in 3% sodium chloride in distilled water was studied under CO2 and H2S gas mixtures (varying from 7 (483) to 72 (496) psi (Pa), and from 0.0017 (12) to 0.0060 (41) psi (Pa), respectively) at 100 °F (38 °C). Corrosion rates were determined through a coupon weight loss technique for both steels. In general, as CO2 partial pressure was augmented, corrosion rates increased for a given H2S partial pressure regardless of the type of steel. Nonetheless, as H2S partial pressure was increased (for a given CO2 partial pressure), corrosion rates varied differently according to the type of steel tested. For API 5L grade B, with incremental H2S levels, corrosion rates reached a maximum to then decrease, whereas for API 5L grade X52, corrosions rates kept increasing with H2S partial pressure.
Corrosion behavior of American Petroleum Institute (API) 5L grade B and X52 steels in 3% sodium chloride in distilled water was studied under CO2 and H2S gas mixtures (varying from 7 (483) to 72 (496) psi (Pa), and from 0.0017 (12) to 0.0060 (41) psi (Pa), respectively) at 100 °F (38 °C). Corrosion rates were determined through a coupon weight loss technique for both steels. In general, as CO2 partial pressure was augmented, corrosion rates increased for a given H2S partial pressure regardless of the type of steel. Nonetheless, as H2S partial pressure was increased (for a given CO2 partial pressure), corrosion rates varied differently according to the type of steel tested. For API 5L grade B, with incremental H2S levels, corrosion rates reached a maximum to then decrease, whereas for API 5L grade X52, corrosions rates kept increasing with H2S partial pressure.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 00040 EFFECT OF CRUDE OIL CONTAMINANTS ON THE
Available for download

00040 EFFECT OF CRUDE OIL CONTAMINANTS ON THE INTERNAL CORROSION IN GAS PIPELINES

Product Number: 51300-00040-SG
ISBN: 00040 2000 CP
Author: J.L. Morales, J.J. Perdomo, M. Ramirez, A. Viloria
$20.00
Picture for 00005 PROTECTIVE PROPERTIES OF CRUDE OILS
Available for download

00005 PROTECTIVE PROPERTIES OF CRUDE OILS IN CO2 AND H2S CORROSION

Product Number: 51300-00005-SG
ISBN: 00005 2000 CP
Author: Marta Castillo, Hern~in Rincon, Simona Duplat, Jose Vera, Evaristo Baron
$20.00
Picture for 00023 EFFECT OF STEEL MICROSTRUCTURE AND
Available for download

00023 EFFECT OF STEEL MICROSTRUCTURE AND COMPOSITION ON INHIBITION OF CO2 CORROSION

Product Number: 51300-00023-SG
ISBN: 00023 2000 CP
Author: Egil Gulbrandsen, Rolf Nyborg, Trine Loland, Kemal Nisancioglu
$20.00