04528 High Temperature Electrochemical Corrosion Rate Probes for Combustion Environments

Electrochemical corrosion rate probes have been constructed and tested along with mass loss coupons in an air plus water vapor and a N2/O2/CO2 plus water vapor environment. Temperatures ranged from 200º to 700ºC. Results show that electrochemical corrosion rates for ash-covered mild steel are a function of time, temperature and process environment.

 

 

Product Number: 51300-04528-SG
ISBN: 04528 2004 CP
Author: Bernard S. Covino Jr., Sophie J. Bullard, Stephen D. Cramer, Gordon R. Holcomb, and Malgorzata Ziome
Publication Date: 2005
$0.00
$20.00
$20.00

Electrochemical corrosion rate probes have been constructed and tested along with mass loss coupons in an air plus water vapor and a N2/O2/CO2 plus water vapor environment. Temperatures ranged from 200º to 700ºC. Results show that electrochemical corrosion rates for ash-covered mild steel are a function of time, temperature and process environment. Correlation between the electrochemical and mass loss corrosion rates was poor.

 

Keywords: corrosion, coal combustion, gaseous, electrochemical noise, harmonic distortion, linear polarization resistance, high temperature.

Electrochemical corrosion rate probes have been constructed and tested along with mass loss coupons in an air plus water vapor and a N2/O2/CO2 plus water vapor environment. Temperatures ranged from 200º to 700ºC. Results show that electrochemical corrosion rates for ash-covered mild steel are a function of time, temperature and process environment. Correlation between the electrochemical and mass loss corrosion rates was poor.

 

Keywords: corrosion, coal combustion, gaseous, electrochemical noise, harmonic distortion, linear polarization resistance, high temperature.

PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Also Purchased
Picture for 10008 High Temperature Cathodic Disbondment Tests
Available for download

10008 High Temperature Cathodic Disbondment Tests

Product Number: 51300-10008-SG
ISBN: 10008 2010 CP
Author: Amal Al-Borno, Ph.D., Mick Brown, Ph.D., and Sherry Rao, M.Sc.
Publication Date: 2010
$20.00
Picture for 10007 Test Method for Studying Cathodic Disbonding at High Temperature
Available for download

10007 Test Method for Studying Cathodic Disbonding at High Temperature

Product Number: 51300-10007-SG
ISBN: 10007 2010 CP
Author: Ole Oystein Knudsen, Tor Gunnar Eggen and Kristian Karlsen Brende
Publication Date: 2010
$20.00