97046 THE USE OF ACPD TECHNIQUE IN ASSESSING CRACKING PROPAGATION AND KISSCC OF HIGH STRENGTH OCTG MATERIALS IN SOUR MEDIA

Product Number: 51300-97046-SG
ISBN: 97046 1997 CP
Author: R. Case, C. Sequera, J. R.Vera
$0.00
$20.00
$20.00
This paper describes the use of the alternate torrent potential drop as a method for measuring crack growth continuously throughout testing time, in double cantilever beam (DCB) specimens used for assessing the threshold stress concentration for sulfide stress corrosion cracking or KISS CC. This methodology was used to asses the sulfilde stress corrosion cracking (SSCC) susceptibility in different oil country tubular products (OCTG) grade steels in several conditions. KEYWORDS: SSCC, High strength steels, Fracture Mechanics, Sour Service, Testing Criteria
This paper describes the use of the alternate torrent potential drop as a method for measuring crack growth continuously throughout testing time, in double cantilever beam (DCB) specimens used for assessing the threshold stress concentration for sulfide stress corrosion cracking or KISS CC. This methodology was used to asses the sulfilde stress corrosion cracking (SSCC) susceptibility in different oil country tubular products (OCTG) grade steels in several conditions. KEYWORDS: SSCC, High strength steels, Fracture Mechanics, Sour Service, Testing Criteria
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 97041 EFFECT OF COLD WORKING ON SSC
Available for download

97041 EFFECT OF COLD WORKING ON SSC RESISTANCE OF CARBON AND LOW ALLOY STEELS - A REVIEW

Product Number: 51300-97041-SG
ISBN: 97041 1997 CP
Author: Richard S. Trescder, Robert P. Badrak
$20.00
Picture for 07562 AN INTEGRATED TOOL TO SELECT OCTG MATERIALS
Available for download

07562 AN INTEGRATED TOOL TO SELECT OCTG MATERIALS

Product Number: 51300-07562-SG
ISBN: 07562 2007 CP
Author: Teresa E. Perez, Claudio Morales, Sergio Ferro, and Marcela Goldschmit
Publication Date: 2007
$20.00
Picture for 97047 THE RELATIONSHIP BETWEEN HYDROGEN
Available for download