98013 EFFECT OF PRECORROSION ON THE PERFORMANCE OF INHIBITORS FOR CO2 CORROSION OF CARBON STEEL

Product Number: 51300-98013-SG
ISBN: 98013 1998 CP
Author: E.Gulbrandsen, S.Nesic, A. Stangeland, T. Burchardt, B. Sundfer, S.M.Hesjevik, S.Skjerve
$0.00
$20.00
$20.00
Four commercially available, water soluble corrosion inhibitors for CO2 corrosion have been tested in the laboratoy on carbon steel specimens that were corroded for up to 18 days in the medium prior to inhibitor addition. The tests were performed at 20-50°C, pH 5, 1 bar CO2, 1-3 w% NaCl in glass cells and a glass loop. The results show that inhibitor performances were impaired with increasing precorrosion time and increasing temperature. The resulting corrosion attack was localised within deep pits. The detrimental effect is influenced both by the nature of the steel and the inhibitor composition. The inhibitor failure is related to the formation of a cementite layer at the steel surface. Keywords: carbon dioxide, carbon steel, inhibitors, precomosion, cementite, galvanic coupling
Four commercially available, water soluble corrosion inhibitors for CO2 corrosion have been tested in the laboratoy on carbon steel specimens that were corroded for up to 18 days in the medium prior to inhibitor addition. The tests were performed at 20-50°C, pH 5, 1 bar CO2, 1-3 w% NaCl in glass cells and a glass loop. The results show that inhibitor performances were impaired with increasing precorrosion time and increasing temperature. The resulting corrosion attack was localised within deep pits. The detrimental effect is influenced both by the nature of the steel and the inhibitor composition. The inhibitor failure is related to the formation of a cementite layer at the steel surface. Keywords: carbon dioxide, carbon steel, inhibitors, precomosion, cementite, galvanic coupling
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 98017 MOLECULAR MODELING OF THE INHIBITION
Available for download

98017 MOLECULAR MODELING OF THE INHIBITION OF MILD STEEL CO2 CORROSION BY IMIDAZOLINES

Product Number: 51300-98017-SG
ISBN: 98017 1998 CP
Author: S. Ramachandran, V. Jovancicevic
$20.00
Picture for 98015 Controlling C02 Corrosion with Inhibitor
Available for download

98015 Controlling CO2 Corrosion with Inhibitor

Product Number: 51300-98015-SG
ISBN: 98015 1998 CP
Author: J. A. Dougherty
$20.00