51318-11200-Alloy 699 XA: A new Alloy for Application in Petrochemical Industry under Metal Dusting Condititions

Alloy 699 XA is a new alloy, which was developed for application in petrochemical industry under metal dusting conditions at high pressure. It contains 30% chromium and 2% aluminum.

Product Number: 51318-11200-SG
Author: Heike Hattendorf / Jutta Kloewer / Alejandra López
Publication Date: 2018
$0.00
$20.00
$20.00

Alloy 699 XA is a new alloy, which was developed for application in petrochemical industry under metal dusting conditions at high pressure. It contains 30% chromium and 2% aluminum. Due to this it showed a remarkable larger time to first pit in comparison to N06025 and N06690 in an examination in the highly carburization metal dusting gas 37% CO, 9% H2O, 7% CO2, 46% H2, at 600 °C at 20 bar. Strength properties and creep properties are similar or better than N06601. Ductility at room temperature is comparable to N06601. The Charpy V-notch impact energy and the elongation in a tensile test at 600°C are still above the lower limits after aging solution annealed samples for 3000 h at 600°C. Welding procedure test according to DIN EN ISO 15614-1 was successfully done on 16 mm plate with a matching filler metal. Alloy 699 XA has been produced as plate, bar, seamless tube and wire.

Key words: Alloy 699 XA, metal dusting, creep strength, ductility at room temperature, V- notch impact energy, welding, plate, bar, tube, wire

Alloy 699 XA is a new alloy, which was developed for application in petrochemical industry under metal dusting conditions at high pressure. It contains 30% chromium and 2% aluminum. Due to this it showed a remarkable larger time to first pit in comparison to N06025 and N06690 in an examination in the highly carburization metal dusting gas 37% CO, 9% H2O, 7% CO2, 46% H2, at 600 °C at 20 bar. Strength properties and creep properties are similar or better than N06601. Ductility at room temperature is comparable to N06601. The Charpy V-notch impact energy and the elongation in a tensile test at 600°C are still above the lower limits after aging solution annealed samples for 3000 h at 600°C. Welding procedure test according to DIN EN ISO 15614-1 was successfully done on 16 mm plate with a matching filler metal. Alloy 699 XA has been produced as plate, bar, seamless tube and wire.

Key words: Alloy 699 XA, metal dusting, creep strength, ductility at room temperature, V- notch impact energy, welding, plate, bar, tube, wire

Also Purchased
Picture for 00257 Alloy Selection for Environments Which
Available for download

00257 Alloy Selection for Environments Which Promote Metal Dusting

Product Number: 51300-00257-SG
ISBN: 00257 2000 CP
Author: Brian A. Baker and Gaylord D. Smith
$20.00